CoCr bonding alloy with very high reliability potential during processing. Excellent casting behavior, including vacuum/pressure casting.
Advantages:

  • reliable melting and casting characteristics, especially with vacuum/pressure casting, resulting from the narrow melting range
  • small ingots (4 g) allow exact dosage of the alloy: ideal and economical filling of the crucible
  • no danger of spattering or increased slagging
  • high mechanical strength thanks to tantalum-based crystal solidification
  • enhanced firing behavior of the veneering ceramic through low oxidation
  • radiant luster due to high Cr content

Indication:

  • Maryland bridges
  • crowns and bridges
  • double crowns
  • implant supported supra-structures
  • metal ceramics
  • secondary parts for cast partial dentures (combination works)

Norm: DIN EN ISO 22674 (Type 5), DIN EN ISO 9693

Technical data
Solidus temperature: 1329 ℃ / 2424.2 ℉
Hardness: 340 HV 10
0.2% Yield strength Rp0.2: 760 MPa
Tensile strength Rm: 940 MPa
Modulus of elasticity E: 211 GPa
Elongation A5: 5.3 %
Weight of casting ingot: 4 g
CTE 25 ℃ - 500 ℃ / 77 ℉ - 932 ℉: 14.4 x 10-6 K-1
Liquidus temperature: 1385 ℃ / 2525 ℉
Density: 8.6 g/cm3

Alloy composition
Co: 58.0 %
Cr: 30.0 %
W: 5.5 %
Mo: 3.0 %
Si: 1.5 %
Ta: 1.25 %
Other elements < 1 %: N