- Home /
- CAD/CAM MATERIALS /
- Titanium blanks /
- rematitan Blank Ti5 12Mm
Shop Now
-
Orthodontics
- Hygiene
- Adhesives
- Anchorage System - tomas®
- Archwires
- Bands
- Bracket Systems
- Buccal Tubes
- Class II Appliances
- Equipment
- Expansion Screws
- Intra- / Extra-oral
- Lingual System
- Orthodontic Acrylics
- Pliers and Instruments
- Supplies
- Wires - Wire Elements
-
Prosthetics
-
Ceramics
- Press Ceramic
- Accessories
-
ceraMotion Veneering Ceramics
- CeraMotion Lf - Low-fusing
- ceraMotion Me - Metal
- CeraMotion Ti - Titanium
- CeraMotion Zr - Zirconia
- ceraMotion Zirc ME Ti
- ceraMotion ME TI LF & Zirc
- CeraMotion Me Veneering ceram
- ceraMotion ME TI & LF
- ceraMotion ME Ti LF
- CeraMotion One Touch Liquid
- ceraMotion ME TI & Zirc
- CeraMotion Me Value Concept
- CeraMotion Zr Veneering ceram
- ceraMotion ME TI & Zirc &LF
- ceraMotion Press Ceramic
- ceraMotion Ceramic in Paste
- Crown and Bridge
- Equipment
- Finishing
- Model Casting
- Orthodontic Acrylics
- Prosthetics
-
Ceramics
- CAD/CAM MATERIALS
- KNOWLEDGE
rematitan Blank Ti5 12Mm
Downloads
Description
Titanium alloy (Ti Al6 V4) with increased mechanical hardness. Particularly suitable for long-span, delicate framework structures and for implant work.
Product advantages:
- high mechanical strength
- high level of biocompatibility in implant quality
- ideal for ceramic veneering using bonding ceramics suitable for titanium such as ceraMotion®?Ti
- high degree of corrosion resistance
Color: grey
⌀: 98.4 mm
Thickness: 12 mm
Border: 10 mm
Titanium grade: 5
Norm: DIN EN ISO 22674 (Type 4)
Indication: for all constructions manufactured using milling technique such as crowns, bridges, supra-structures, and also ceramic bonding with suitable ceramics
Technical data
Liquidus temperature: 1650 ℃ / 3002 ℉
Elongation A5: 7 %
Tensile strength Rm: 908 MPa
Modulus of elasticity E: 120 GPa
Solidus temperature: 1605 ℃ / 2921 ℉
Hardness: 285 HV 10
0.2% Yield strength Rp0.2: 832 MPa
CTE 25 ℃ - 500 ℃ / 77 ℉ - 932 ℉: 10.0 x 10-6 K-1
Density: 4.3 g/cm3
Alloy composition
Ti: 90 %
Al: 6 %
V: 4 %
Fe: <1 %
O: <1 %